Cobalt Hydroxide Jet Milling Project for a Korean Battery Materials Producer

1. 프로젝트 개요

위치: 한국

재료: Cobalt hydroxide, Co(OH)₂. A battery precursor feed that dries into hard agglomerates and must be broken without adding metal contamination.

핵심 목표: Deagglomerate dried cobalt hydroxide to D50 10–15 μm, with product aluminum below 2,000 ppm. The customer needed a dry route to replace hammering and screening.

장비: Epic Powder MQW03 Jet Mill

2. 기술적 매개변수 및 제품 사양

The trial run measured the following values on the customer’s dried cobalt hydroxide:

목	기술 데이터
Final Fineness (D50)	10–15 μm
시간당 수용 능력	60–110 kg/h
Product Aluminum (Al)	< 2,000 ppm
Feed Moisture	< 0.5%
사료 크기	30–100 μm, agglomerated after drying
장비 유형	MQW03 Jet Mill

3. 프로젝트 주요 성과

A. Metal-Free Product Path

The MQW03 grinds by particle-on-particle collision. Compressed gas accelerates the feed, and the particles break against each other. No grinding media touches the product. This configuration kept product aluminum below 2,000 ppm, against a feed that measured 10,000 ppm in the dried NCM trial on the same platform.

B. Cut Point Set from the Control Panel

The classifier cut point is adjustable from the control panel. The customer specified D50 10–15 μm, and we set the machine to that target before the trial. The trial run matched the agreed specification without a mechanical change.

C. Capacity Matched to the Customer’s Line

The trial held 50–100 kg/h at the target fineness. This range covers the customer’s pilot and small production demand. The same unit will move into their line after shipment.

4. 프로세스 흐름

Drying: The customer dries Co(OH)₂ to under 0.5% moisture.
집적: The dried feed leaves the dryer as hard cakes, 30–100 μm.
Previous breakage step: Hammers and screens break the cakes. This step adds steel to the precursor feed.
Jet milling: Dried agglomerates enter the MQW03. Compressed gas accelerates the particles, and they break against each other. No grinding media touches the product.
분류: The classifier returns coarse particles to the grinding zone. Product at D50 10–15 μm passes through.
수집: The product leaves the mill through the discharge at 60–110 kg/h.

5. 결론

This project shows what the MQW03 does on a dried precursor feed: it breaks agglomerates without metal contact and holds the cut point at D50 10–15 μm. Producers with cobalt hydroxide or dried NCM that cakes in drying or transit can check the trial report against their own feed.